Table 1

Summary of monolayered phantoms composition. All phantoms are made of a PDMS matrix including scattering particles of different materials, sizes and concentrations.

Phantom Particle material Refractive index Size Density (% weight of PDMS) μs target g target
No. 0 TiO2 2.29 <5 μm 0.40%
No. 1 TiO2 2.29 800 nm 0.13% 1.8 mm−1 0.6
No. 2 TiO2 2.29 <5 μm 0.30%
No. 3 TiO2 2.29 800 nm 1.34% 18 mm−1 0.6
No. 4 ZnO 1.96 800 nm 0.12% 1.4 mm−1 0.8
No. 5 ZnO 1.96 800 nm 1.19% 14 mm−1 0.8
No. 6 SiO2 1.54 400 nm 1.27% 1 mm−1 0.7
No. 7 SiO2 1.54 400 nm 12.7% 10 mm−1 0.7
No. 8 SiO2 1.54 1 μm 0.38% 1 mm−1 0.9
No. 9 SiO2 1.54 1 μm 3.81% 10 mm−1 0.9

Current usage metrics show cumulative count of Article Views (full-text article views including HTML views, PDF and ePub downloads, according to the available data) and Abstracts Views on Vision4Press platform.

Data correspond to usage on the plateform after 2015. The current usage metrics is available 48-96 hours after online publication and is updated daily on week days.

Initial download of the metrics may take a while.